EFFECT OF THE AMOUNT OF Si AND AGING DURATIONS IN Al2024-Si ALLOYED COMPOSITES PRODUCED BY POWDER METALLURGY METHOD

Yıl 2017, Cilt: 6 Sayı: 1, 226 - 231, 31.01.2017
https://doi.org/10.28948/ngumuh.298165

Öz

   In the present paper, different weight fractions of 5, 10 and 15% Si particles reinforced Al2024 matrix
composites were prepared by the powder metallurgy method. The powders were prepared using a digital
weighing scale with a precision of 0.0001. The powders were stirred with turbulo machine for 1 hour.
Homogeneously mixed powders were pressed to form 12 mm in diameter and 10 mm height block in one
direction. The pressed samples were sintered gradually first at 300ºC for 30 min then 590°C for 90 min in an
argon atmosphere. Sintered samples were applied aging treatment by different parameters. The effects of Si
addition and aging time on hardness behaviour of composites have been investigated.

Kaynakça

  • JUN, D., LIU, Y.H., YU, S.R., LI, W.F., “Dry Sliding Friction and Wear Properties of Al2O3 and Carbon Short Fibres Reinforced Al-12Si Alloy Hybrid Composites”, Wear, 257, 930-940, 2004.
  • KAW, A.K., “Mechanics of Composite Materials”, Crc Press, Washington, 3, 61- 65, 1997.
  • HULL, D., CLYNE, T.W., “An Introduction to Composite Materials”, 2nd Edition, Cambridge University Press, Cambridge, 1996.

TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ

Yıl 2017, Cilt: 6 Sayı: 1, 226 - 231, 31.01.2017
https://doi.org/10.28948/ngumuh.298165

Öz

   Al2024 matrisli Si takviyeli kompozitler, Al2024 alaşım tozlarının içerisine ağırlıkça ayrı ayrı %5, 10 ve 15
oranında Si ilavesi yapılarak klasik Toz Metalürjisi yöntemiyle üretilmiştir. Tozlar 0,0001 hassasiyetli terazi ile
tartılarak, üç eksenli karışım yapan turbulo cihazında bir saat süreyle karıştırılmıştır. Elde edilen karışım tozlar
12 mm çapında 10 mm yüksekliğinde blok oluşturacak şekilde tek eksenli pres ile blok haline getirilmiştir. Blok
haline getirilen numuneler kademeli olarak önce 300°C'de 30 dakika, ardından 590°C'de 90 dakika bekletilerek
sinterlenmiştir. Üretilen numunelere farklı parametrelerde yaşlandırma işlemi uygulanarak, kompozitlerde
yaşlandırma süresinin ve Si miktarının sertlik özelliklerine etkisi incelenmiştir. 

Kaynakça

  • JUN, D., LIU, Y.H., YU, S.R., LI, W.F., “Dry Sliding Friction and Wear Properties of Al2O3 and Carbon Short Fibres Reinforced Al-12Si Alloy Hybrid Composites”, Wear, 257, 930-940, 2004.
  • KAW, A.K., “Mechanics of Composite Materials”, Crc Press, Washington, 3, 61- 65, 1997.
  • HULL, D., CLYNE, T.W., “An Introduction to Composite Materials”, 2nd Edition, Cambridge University Press, Cambridge, 1996.
Toplam 3 adet kaynakça vardır.

Ayrıntılar

Konular Malzeme Üretim Teknolojileri
Bölüm Malzeme ve Metalürji Mühendisliği
Yazarlar

Hasan Karabulut

Mustafa Türkmen Bu kişi benim

Yayımlanma Tarihi 31 Ocak 2017
Gönderilme Tarihi 23 Mayıs 2016
Kabul Tarihi 22 Eylül 2016
Yayımlandığı Sayı Yıl 2017 Cilt: 6 Sayı: 1

Kaynak Göster

APA Karabulut, H., & Türkmen, M. (2017). TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi, 6(1), 226-231. https://doi.org/10.28948/ngumuh.298165
AMA Karabulut H, Türkmen M. TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ. NÖHÜ Müh. Bilim. Derg. Ocak 2017;6(1):226-231. doi:10.28948/ngumuh.298165
Chicago Karabulut, Hasan, ve Mustafa Türkmen. “TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ”. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi 6, sy. 1 (Ocak 2017): 226-31. https://doi.org/10.28948/ngumuh.298165.
EndNote Karabulut H, Türkmen M (01 Ocak 2017) TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi 6 1 226–231.
IEEE H. Karabulut ve M. Türkmen, “TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ”, NÖHÜ Müh. Bilim. Derg., c. 6, sy. 1, ss. 226–231, 2017, doi: 10.28948/ngumuh.298165.
ISNAD Karabulut, Hasan - Türkmen, Mustafa. “TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ”. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi 6/1 (Ocak 2017), 226-231. https://doi.org/10.28948/ngumuh.298165.
JAMA Karabulut H, Türkmen M. TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ. NÖHÜ Müh. Bilim. Derg. 2017;6:226–231.
MLA Karabulut, Hasan ve Mustafa Türkmen. “TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ”. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi, c. 6, sy. 1, 2017, ss. 226-31, doi:10.28948/ngumuh.298165.
Vancouver Karabulut H, Türkmen M. TOZ METALURJİSİ YÖNTEMİ İLE ÜRETİLEN Al2024-Si ALAŞIMI KOMPOZİTLERDE Si MİKTARININ VE YAŞLANDIRMA SÜRELERİNİN ETKİSİ. NÖHÜ Müh. Bilim. Derg. 2017;6(1):226-31.

download